masterbatch ti a ṣe atunṣe fun awọn bellows polyethylene iwuwo giga pẹlu iwọn ila opin nla
Masterbatch ti a ṣe atunṣe fun awọn bellows polyethylene iwuwo giga pẹlu iwọn ila opin nla,
HDPE fun isalẹ, HDPE fun paipu curraged,
Ọja yii jẹ iṣelọpọ nipa lilo imọ-ẹrọ ilana UNIPOL™.O ti pinnu fun lilo ninu awọn ohun elo paipu nibiti agbara hydrostatic igba pipẹ ati atako lati fa fifalẹ idagbasoke kiraki ni o fẹ.Awọn ohun elo ti o yẹ pẹlu awọn paipu pinpin gaasi adayeba, fifin ile-iṣẹ iwọn ila opin nla, iwakusa, omi eeri, ati awọn laini iṣẹ omi ti ilu.Ibamu Awọn ajohunše Ile-iṣẹ: ASTM D 3350: isọdi sẹẹli – Adayeba – PE345464A – Dudu – PE345464C (Wo Awọn AKIYESI A) Plastics Pipe Institute (PPI): TR-4 – Adayeba Pipe – DGDB-2480 NT 3408 — ASTM PE3608 paipu 0p 160p HDsiB. @ 73°F – Dudu Pipe – DGDB-2480 BK 3408 (Wo ALAYE B) — ASTM PE3608 paipu ite – 1600psi HDB @ 73°F ati 800psi HDB @ 140°F National Sanitation Foundation (NSF) Standard 14 ati 61 – Adayeba Pipe - DGDB-2480 NT 3608 - Black Pipe - DGDB-2480 BK 3608 (Wo awọn AKIYESI B) Kan si awọn ilana fun awọn alaye pipe.AKIYESI: (A) Awọn nọmba marun akọkọ ti iyasọtọ sẹẹli da lori resini adayeba.Nọmba ti o kẹhin ati lẹta da lori resini dudu (resini adayeba pẹlu 6.5% DFNF-0092).(B) Resini adayeba extruded labẹ awọn ipo to dara pẹlu erogba dudu masterbatch DFNF-0092 (6.5%).
Nlo
Awọn ohun elo 1.Pipe
2.Natural gaasi pinpin oniho
3.Large opin ise fifi ọpa
4.Iwakusa
5.Eto omi
6.Municipal omi iṣẹ laini
HDPEBellows, mọ bi PE curragted paipu, jẹ titun kan Iru ina paipu ṣe ti ga iwuwo polyethylene.It ni o ni awọn abuda kan ti ina àdánù, ga titẹ resistance, ti o dara toughness, awọn ọna ikole ati ki o gun aye.
Awọn iwọn ila opin ti HDPE ni ilopo-odi Bellows ti a ṣe ni China ni φ400 ~ φ1400mm, eyi ti ko nikan nilo ga fluidity ti awọn ohun elo lati pade awọn processing awọn ibeere ti awọn ẹrọ, sugbon tun pàdé awọn ibeere ti iwọn stiffness ite ti awọn ọja (S2 kilasi jẹ tobi ju 8KN). / m2, fun awọn ohun elo kan, ti o tobi ni iwọn ila opin, isalẹ awọn iwọn wiwọn lile iye.Nitorina eyi mu iṣoro kan wa si yiyan awọn ohun elo. ọja naa ko le de ọdọ 8KN / m2. Iwọn idanwo lile iwọn ni iwọn otutu (23 ± 2 ℃) jẹ 6.2kN / m2, eyiti o nilo iyipada ti ohun elo ati pe o nilo pe laisi idinku iṣẹ ti atilẹba HDPE2480. Iyẹn ni, Labẹ ipo ti aridaju irọrun iwọn, iwọn otutu kekere ati agbara ikolu ogbontarigi ti ọja; Ṣe ilọsiwaju atunse ti awọn ohun elo lati rii daju ite ti lile ọja.
Ilana iṣelọpọ fun kikun kikun ti a ṣe atunṣe masterbatch ti iwọn giga giga iwuwo giga ti polyethylene bellows eyiti o le pade awọn ibeere ti irọrun iwọn iwọn alaja nla, ipa iwọn otutu kekere, agbara ipa ogbontarigi ati diẹ ninu atunse ku.
Ti a dapọ pẹlu 30-50% D50 = 2-7 μm ultrafine calcium carbonate ati 50-70% ultrafine talc lulú, a ti pese erupẹ apapo.
Iwọn kikun ti ohun elo titunto si ti a ṣe ti ohun elo iyẹfun apapo le de ọdọ 50% ni awọn bellows dimeter-nla HDPE.Labẹ ipo ti HDPE∶ ohun elo titun ti a tunṣe = 50∶50, iwuwo paipu pẹlu alaja kanna pọ si 5 ~ 6% nikan, ati pe modulu titan jẹ to 1360Mpa.Imudani ati ipa ipa ti ohun elo pẹlu agbara iyipada ti 24Mpa jẹ iru si ti ohun elo ti a ṣe atunṣe atilẹba nigbati o ba kun pẹlu 30%: agbara fifẹ jẹ ≥24Mpa, ati nọmba rupture ti awọn ayẹwo 10 pẹlu ipakokoro ipa ni 0 ℃ jẹ kere ju 1, eyiti o ni kikun pade awọn ibeere didara ti awọn bellows HDPE nla-caliber.
Nlo 30 ~ 50% D50 = 2 ~ 7μm superfine calcium carbonate ati 50 ~ 70% superfine talc lulú lati dapọ sinu 100-apakan powder powder, fifi 0.2 ~ 1 apakan idapọmọra oluranlowo sinu iyẹfun apapo ati igbiyanju fun 5 ~ 10 iṣẹju ni 120 ~ 140 ℃.Lẹhinna ṣafikun awọn ẹya 3 ~ 6 ti epo funfun, 1 ~ 2 awọn ẹya ti stearic acid, 1 ~ 2 awọn ẹya ti epo silikoni hydroxyl ati awọn ẹya 20 ~ 30 ti polyethylene tabi polypropylene aruwo paapaa lẹhin ohun elo naa, ni iwọn otutu 150 ~ 190 ℃, nipasẹ ni afiwe ibeji dabaru extruder awọn oniwe-adalu extrusion ati granulating.
Lati le ṣọkan iwọn ti masterbatch ati dinku egbin ati eruku ninu ilana iṣelọpọ, masterbatch ti ge ati iboju nipasẹ afẹfẹ lati gba iwọn patiku kanna.
Aṣoju idapọ jẹ aṣoju titaniji titanate tabi aluminate asopo asopọ tabi oluranlowo silane.